Basic Info.
Model NO.
TB003
Supply State
Sintered, Forged and Vacuum Treatment
Customized
Sheet/Plate/Foil/Strip According to Drawi
Material
90%-97%Wnife or 90%-97%Wnicu
Grade
ASTM B777-15 AMS 7725ctams T-21014
Density
16.85~17.30g/Cc, 17.15~17.85g/Cc, 18.25~18.85g/Cc
Ultimate Tensile Strength
758MPa, 724MPa, 689MPa
Class
1, 2, 3, 4
Yield Strength
517MPa
Elongation
5%, 3%, 2%
Nonmagnetic Alloys
Ultimate Strength 648MPa, 648MPa, Na
Nonmagnetic Yield Strength
517MPa, Na
Nonmagnetic Elongation
2%, 1%, Na
Transport Package
Export Wooden Box with Foam Inside
Specification
Standard sizes or customized
Trademark
Kefeng
Origin
China
HS Code
81019910
Product Description
Kefeng's Tungsten bucking bars provide increased weight (density) to allow riveting in confined areas. The weight to size ratio provides a good kinetic energy transfer to expedite the rivet installation process. Our Tungsten bucking bars greatly reduce the vibration caused by driving rivets reducing or eliminating damage to the hand. They are precision ground with polished surface fora professional look in your set rivets. Kefeng tungsten bucking bars are available in standard sizes and shapes customized or clients drawings.
High-density ergonomic tungsten bucking bar rivet blocks reduce vibration and kickback while riveting in aircraft operations. Repeated vibrations can cause wrist strain and fatigue, and regular steel bucking bars don't fully protect the riveter from the harmful effects. Tungsten material bucking bars, over twice as dense as normal steel, absorbs the shock, allowing you to rivet more effectively for a longer period of time.
High Density Aircraft Tool Tungsten Heavy Alloy Bucking Bars, customized.
Name: Tungsten alloy Bucking Bar
Material: 90%-97%WNiFe or WNiCu
Standard: AMS-T-21014 and ASTM-B-777
Size: Customized or as per customer's drawings
Package: Export cases (Wooden cases or Iron Drums)
Payment: Usually T/T and L/C, D/A can be accepted.
Characteristics and features
Tungsten alloy offer the maximum density available, these tungsten alloy bars are more than twice as heavy as an identical bar made of steel, small size and high density make the bars can fit small areas.
Small size and same weight ,tungsten alloy bucking bars reduce the recoil when reflecting the impact back to the rivet shaft. Bars that are more massive can reduce vibration transmitted to the hand. Tungsten alloy bucking bar makes any riveting process much easier, provide a good kinetic energy transfer to expedite the rivet installation process thus can greatly reduce the vibration caused by driving rivets and eliminate damage to operators' hands.
- High temperature resistance
- High impact and crack resistance
- Shock and corrosion resistance
- Good modulus of elasticity and high hardness
Application
The Hand Tool Riveting Tool Tungsten Bucking Bars are mostly used in aviation, aerospace and aircraft industries. Other applications for tungsten heavy alloy machining parts:
- Radiation shielding
- Containers of radioactive isotopes
- High performance projectiles for underwater hunting
- Gyro components
- Balance weights for racing boats and racing cars
- The optical industry like microscopes and measuring instruments.
Technical parameters
Tungsten heavy alloy | WNiFe (ASTM B777, AMS-T-21014) | WNiCu (ASTM B777, AMS-T-21014) | |||||
| Designation | 90W | 93W | 95W | 97W | 90W | 93W | 95W |
| Density g/cm3) | 16.85~17.30 | 17.15~17.85 | 17.75~18.35 | 18.25~18.85 | 16.85~17.30 | 17.15~17.85 | 17.75~18.35 |
| Tensile Strength (MPa) | 758Min | 758Min | 724Min | 689Min | 648Min | 648Min | 648Min |
| Elongation (%) | 5Min | 5Min | 3Min | 2Min | 2Min | 2Min | 1Min |
| Hardness (HRC) | 32Max | 33Max | 34Max | 35Max | 32Max | 33Max | 34Max |
| Yield strength(MPa) | 517Min | 517Min | 517Min | 517Min | 517Min | 517Min | 517Min |
Our Quality Assurance
Our Test Equipment
We offer the test report including all relevant technical data for the properties of physical, material, chemical ects for all finished products.